Method of forming a solder bump structure

ABSTRACT

A method of the present invention includes preparing a substrate having a surface on which a electrode pad is formed, forming a resist layer on the substrate, the resist layer having an opening on the electrode pad, filling conductive paste in the opening of the resist layer; sintering the conductive paste in the opening to form a conductive layer which covers a side wall of the resist layer and a surface of the electrode pad in the opening, a space on the conductive layer leading to the upper end of the opening being formed, filling solder in the space on the conductive layer and removing the resist layer.

BACKGROUND OF THE INVENTION Technical Field

The present invention relates to a method of forming a solder bump structure, and more specifically, to a method of forming a solder bump structure using metal paste and molten solder.

Description of the Related Art

While performance and function of electronics devices improve highly, the flip chip packaging is broadly applied from the consumer product represented by a smart phone, tablet PC, etc. to the supercomputer. Furthermore, it is predicted that the demand of the flip chip packaging increases sharply by the appearance of the 2.5 or 3-dimensional (2.5D or 3D) stacked device of the semiconductor chip.

In the 2.5D or 3D package, connecting terminals pitch and bump size is dramatically fine. In that case, there is a problem of failure due to stress applied to the junction or failure due to electro migration (EM) caused by the increase of current density. To solve this problem, the solder bumps using Cu pillars corresponding to the miniaturization of the connecting terminals pitch and bump size is mainly used.

Since Cu Pillar is generally formed using electroplating, there is a need for formation and removal (etching) of the seed layer. Therefore, the production cost is relatively high. Further, there is also the use of electroless plating to form the electrode pads under the solder bumps. However, the electroless plating is difficult to process management.

Thus, the formation of the conventional solder bumps needs electroplating/electroless plating that the process cost is high and the process management is difficult. Therefore, there is need to form fine solder bumps without using the plating process.

SUMMARY OF THE INVENTION

The present invention provides a method of forming a solder bump structure without using a plating process. In the method, conductive paste injected in opening of the resist layer is sintered and contracted to form metal pillar (conductive layer) connected to the electrode pad underneath.

The surface of the formed metal pillars (conductive layer) has cone-shaped surface. The cone-shaped surface covers the sidewalls of the openings of the resist layer, and extends upwardly to the entrance opening. Therefore, the contact area with solder formed thereon increases. Furthermore, it is possible to prevent the gas out from the side wall of the resist layer during solder melting (bonding) and the occurrence of incomplete solder fill.

BRIEF DESCRIPTION OF THE DRAWING

FIG. 1 is a chart showing a flow of one embodiment of the method of the present invention.

FIG. 2 is a cross-sectional diagram showing each step in the flow of one embodiment of the method of the present invention.

FIG. 3 is a cross-sectional diagram showing each step in the flow of one embodiment of the method of the present invention.

FIG. 4 is a cross-sectional diagram showing each step in the flow of one embodiment of the method of the present invention.

FIG. 5 is a cross-sectional diagram showing each step in the flow of one embodiment of the method of the present invention.

FIG. 6 is a cross-sectional diagram showing each step in the flow of one embodiment of the method of the present invention.

FIG. 7 is a cross-sectional diagram showing each step in the flow of one embodiment of the method of the present invention.

FIG. 8 is a cross-sectional diagram showing each step in the flow of one embodiment of the method of the present invention.

FIG. 9 is a chart showing a flow of another embodiment of the method of the present invention.

FIG. 10 is a cross-sectional diagram showing each step in the flow of one embodiment of the method of the present invention.

FIG. 11 is a cross-sectional diagram showing each step in the flow of one embodiment of the method of the present invention.

FIG. 12 is a cross-sectional diagram showing each step in the flow of one embodiment of the method of the present invention.

DETAILED DESCRIPTION

The following is an explanation of embodiments of the present invention with reference to the drawings. FIG. 1 is a chart showing a flow of one embodiment of the method of the present invention. Each of FIG. 2 to FIG. 8 shows cross-sectional diagram at each step in the flowchart of FIG. 1. FIG. 9 is a chart showing a flow of another embodiment of the method of the present invention. FIG. 10 to FIG. 12 show cross-sectional diagrams at three steps selected from the flowchart of FIG. 9. Each of the cross-sectional diagrams shows a part of a substrate. The following is an explanation of the embodiments of the method of the present invention with reference to FIG. 1 to FIG. 12.

Embodiment 1

Referring FIG. 1 and FIG. 2, in step S1, a substrate 10 is prepared first. The substrate 10 has a surface on which electrode pads 14 have been formed between patterned insulating layers 12. The electrode pads 14 can include metal such as Aluminum (Al), for example. The insulating layers 12 can include silicon oxide (SiO₂), for example. The substrate 10 can include semiconductor wafer such as a Si wafer, a semiconductor chip/die, or a circuit board. The material of the semiconductor wafer or chip is not limited to specific types. The substrate 10 can include a plurality of wiring layers (including circuits, devices such as a transistor) and insulating layers. The wiring layers can electrically connected to the electrode pads 14. The substrate 10 may include the lamination (stack) of a plurality of semiconductor substrates.

Referring FIG. 3, in step S2, a resist layer 16 is formed on the substrate 10 as shown in FIG. 3. A resist material is applied on the substrate 10 using spin coating for example, and cured the resist material at a predetermined temperature to form the resist layer 16. The resist material may include light (UV)-curable resin (photopolymer) or thermosetting resin (polymer). The resist layer 16 may include one of negative type resist or positive type resist.

Next, the resist layer 16 is exposed using light induced through a photo mask (not shown) in FIG. 3. The exposure is performed to expose only the resist region over the insulating layers 14 without exposing the resist region over the electrode pads 14. Next, the exposed resist layer 16 is developed, and openings 20 are formed over the electrode pads 14 as shown in FIG. 4. The opening 20 exposes the surface of the electrode pad 14 on the substrate 10. When the electrode pad 14 is formed of a metal easily oxidized such as Al, it is necessary to remove the oxide layer formed on the surface before the next step. The oxide layer can be removed by etching using an acidic solution, for example.

Next, in step S3, conductive paste 22 is filled in the opening 20 of the resist layer 18 as shown in FIG. 5. The conductive paste 22 can be filled in the opening 20 of the resist layer 18 using screen-printing technique or injecting technique, for example. The conductive paste 22 can include metal nanoparticles in a solvent. The metal nanoparticles can include at least one of copper (Cu), nickel (Ni), silver (Ag) or gold (Au), for example. The viscosity of the paste and the particle fraction in the paste can be determined in consideration of paste shrinkage, in other words, the thickness of a conductive layer to be obtained by sintering of the next process.

Next, in step S4, the conductive paste 22 in the opening 20 is sintered to form a conductive layer. The sintering of the conductive paste 22 in the opening is performed to heat the conductive paste 22 at 100 to 250 degrees for 0.1 to 2.0 hours in an atmosphere of nitrogen gas or formic acid to prevent oxidation of the metal surface after the sintering. If the sintering is performed in air, it is necessary to remove the oxide layer on the metal surface. In the sintering process, the conductive paste 22 is shrunk so that the conductive layer 24 is formed to cover the side wall of the resist layer 18 and the surface of the electrode pad 14 in the opening 20 as shown in FIG. 6. As solder filling is performed in the next step without additional conductive paste coating, the volume shrinkage of the conductive paste 22 after sintering is optimized. The volume shrinkage of the conductive paste 22 is dependent on the design value of the bump diameter/height, and for example is preferably 50% or more. The conductive layer 24 corresponds to a conventional metal pillar (post). The space 26 is formed on the conductive layer 24 which leads to the upper end of the opening 20. The conductive layer 24 has a cone-shaped surface 28 shown in FIG. 6. The cross-section of the conductive layer 24 has a conformal shape.

Next, in step S5, solder 30 is filled in the space 26 on the conductive layer 24 as shown in FIG. 7. The solder bump structure of FIG. 7 can be used as an embodiment of the present invention. This embodiment can be used for flip-chip bonding after the substrate 10 was divided into a plurality of chips. The solder 30 is injected in the space 26 on the conductive layer 24 using Injection Molded Solder (IMS) process, for example. In the IMS, molten solder is filled in the space under a predetermined pressure. The solder may include a Pb-free solder metal containing at least one metal selected from the group consisting of elemental Sn, Ag, Au, Cu, Ni, Bi, In, Zn, Co, Ge, Fe and Ti, and containing Sn, Bi or In as a main component. The solder 30 has a convex top surface 31. Next, in step S6, the resist layer 18 is removed using etching process and the solder bump structure 33 of the one embodiment of the present invention is formed as shown in FIG. 8. As described above, it may also be used in an embodiment shown in FIG. 7 without removing the resist layer 18.

In the solder bump structure 33, the thickness TC of the central portion 32 of the conductive layer (metal pillar) 24 is in the range of ⅕ to ⅔ of the length TS from the surface of the electrode pad 14 to the top surface of the solder 31. The thickness TC of the central portion 32 of the metal pillar 24 is in the range of 1 to 50 micrometers. After the sintering of the conductive paste 22, the conductive layer 24 is formed on the side wall of the resist layer 18 as described above referring to FIG. 6. Therefore, it expected to improvement of solder wet-ability and solder filling property. Further, in the EM (Electro migration) test, the initial void is easily generated in the periphery of the metal pillar and the electrode pad. However, since the conductive layer 24 on the side wall of the resist layer 18 is formed, it is expected to improve the EM resistance.

Embodiment 2

Referring FIG. 9 to FIG. 12, another embodiment of the method of the present invention is explained. Steps S10 to S40 in FIG. 9 are same as steps S1 to S4 in FIG. 1 as described above. Steps 50 to 70 are added as new steps in FIG. 9. FIG. 10 shows a cross-sectional diagram after step S40 which performs sintering of the conductive paste 22 in the opening 20 in FIG. 5. In FIG. 10, a thin conductive layer 34 is formed after the sintering process. The thin conductive layer 34 covers the side wall of the resist layer 18 and the surface of the electrode pad 14 in the opening 20 as shown in FIG. 10. The thickness TC1 of the central portion 35 of the conductive layer 34 is thinner than the predetermined thickness in the range of 1 to 50 micrometers, for example. Therefore, it is necessary to form additional conductive layers on the conductive layer 34 in order to ensure a predetermined thickness.

In step S50, additional conductive paste 36 is filled in the opening 26 of the resist layer 18 as shown in FIG. 11. The filling of the conductive paste 36 is performed to the upper surface of the opening 26 as step S3 in FIG. 3 described above. In step S60, additional sintering of the conductive paste 36 is performed to form the additional conductive layer 38 on the conductive layer 34 as shown in FIG. 12. In step S70, it is judged whether the total thickness TC2 of the central portion 39 (35) of the conductive layers 34, 38 is over the predetermined thickness TH or not. If the thickness TC2 is smaller than the predetermined thickness TH, step S50 and S60 are repeated until the thickness TC2 is equal to or greater than the predetermined thickness TH.

If the judgment of step S70 is YES, in step S80, solder 30 is filled in the space 40 on the conductive layer 38 as in the case of FIG. 7. The solder 30 is injected in the space 40 on the conductive layer 38 using IMS process, for example. Finally, in step S90, the resist layer 18 is removed using etching process and the solder bump structure of another embodiment of the present invention is formed as in the case of FIG. 8. This embodiment is characterized in that the conductive layer is formed of two or more layers as shown in FIG. 12 in order to obtain the predetermined thickness of the central portion 39 of the conductive layers 34, 38.

Embodiment 3

Referring FIG. 1, FIG. 5, and FIG. 7, another embodiment of the method of the present invention is explained. In this embodiment, the filling of the conductive paste 22 in step S3 of FIG. 1 and FIG. 5 is performed using IMS process which is used in step S5 of filling of solder 30 instead of screen printing. In step S3, the conductive paste 22 is injected in place of solder under predetermined pressure by IMS process. By using the IMS in Step S3, it is possible to perform steps S3 to Step S5 under one IMS process. That is, even sintering of step S4 can be performed in the IMS process. As a result, it is possible to achieve a further shortening of the production time and simplification of the manufacturing process to form the solder bump structure.

The embodiment of the present invention has been described with reference to the accompanying drawings. However, the present invention is not limited to the embodiment. The present invention can be carried out in forms to which various improvements, corrections, and modifications are added based on the knowledge of those skilled in the art without departing from the purpose of the present invention. 

What is claimed is:
 1. A method of forming a solder bump structure, comprising the steps of: filling conductive paste in an opening of a layer formed over an electrode pad; sintering the conductive paste in the opening to cause shrinkage of the conductive paste to form a conductive layer having a cone-shaped surface formed therein, the conductive layer covering a side wall of the opening and a surface of the electrode pad in the opening; and filling solder in the cone-shaped surface on the conductive layer.
 2. The method according to claim 1, wherein the step of filling conductive paste includes a step of screen-printing conductive paste containing metal nanoparticles in a solvent on the substrate.
 3. The method according to claim 1, wherein the step of filling conductive paste includes a step of injecting conductive paste containing metal nanoparticles in a solvent into the opening.
 4. The method according to claim 1, wherein the conductive paste includes at least one of copper, nickel, silver or gold.
 5. The method according to claim 1, wherein a cross-section of the conductive layer has a conformal shape.
 6. The method according to claim 1, wherein a thickness of a central portion of a cross-section of the conductive layer is in a range of ⅕ to ⅔ of a depth of the opening.
 7. The method according to claim 1, further comprising a step of etching a surface of the conductive layer before the step of filling solder in the space on the conductive layer.
 8. The method according to claim 1, further comprising a step of etching a surface of the electrode pad in the opening before the step of filling conductive paste in the opening.
 9. The method according to claim 1, wherein the step of filling conductive paste in the opening includes a step of filling conductive paste in the opening using Injection Molded Solder (IMS) method.
 10. The method according to claim 1, wherein the step of sintering the conductive paste in the opening includes a step of heating the conductive paste in an atmosphere of inert gas or formic acid.
 11. The method according to claim 1, wherein the electrode pad comprises aluminum.
 12. The method according to claim 1, wherein the opening is formed on a resist layer and aligned with the electrode pad.
 13. A method of forming a solder bump structure, comprising the steps of: filling conductive paste in an opening of a layer over an electrode pad; sintering the conductive paste in the opening to cause shrinkage of the conductive paste to form a conductive layer having a cone-shaped surface formed therein, the conductive layer covering a side wall of the opening and a surface of the electrode pad in the opening; filling conductive paste in the cone-shaped surface on the conductive layer; sintering the conductive paste in the cone-shaped surface to form an additional conductive layer on the conductive layer; repeating the step of filling conductive paste in the cone-shaped surface on the conductive layer and the step of sintering the conductive paste in the cone-shaped surface to form the additional conductive layer until a total thickness of the conductive layers becomes a predetermined thickness; and filling solder in a depression on the conductive layers.
 14. The method according to claim 13, wherein the step of filling conductive paste includes a step of screen-printing conductive paste containing metal nanoparticles in a solvent on the substrate.
 15. The method according to claim 13, wherein the step of filling conductive paste includes a step of injecting conductive paste containing metal nanoparticles in a solvent into the opening.
 16. The method according to claim 13, wherein the conductive paste includes at least one of copper, nickel, silver or gold.
 17. The method according to claim 13, wherein a cross-section of the conductive layer has a conformal shape.
 18. The method according to claim 13, further comprising a step of etching a surface of the conductive layers before the step of filling solder in the space on the conductive layers.
 19. The method according to claim 13, further comprising a step of etching a surface of the electrode pad in the opening before the step of filling conductive paste in the opening.
 20. The method according to claim 13, wherein the opening is formed in a resist layer and aligned with the electrode pad. 